menu

Duplex Steel 2205

HomeRound BarsDuplex Steel 2205
HomeRound Bar/Rods

Duplex Steel 2205 Grade Round Bar Best Price in India

Duplex Steel 2205 Material Bar Sizes,Technical Metal Corp. Govt. Approved Supplier & Exporter of Duplex Steel S31803 Round Bar, 2205 round bar, 2205 stainless round bar, saf 2205 round bar, 2205 duplex stainless round bar, alloy 2205 round bar, duplex 2205 round bar

Ready Stock 2205 stainless steel round bar, s31803 bar, s31803 round bar, uns s31803 round bar, uns s31803 bar. Buy Duplex Stainless Steel S31803 Bright Bar in India,.We are Largest Specialist & supplier of Duplex Steel 2205 Grade Round Bar in India

25 years of world class manufacturing of Duplex Steel 2205 Grade Round Bar, renowed & trusted manufacturer, exporter in india of Duplex Steel 2205 Grade Round Bar. manufacturing Duplex Steel 2205 Grade Round Bar as per international standards

Supplying Duplex Steel 2205 In India At Factory Price


  • Bar Specification: ASTM A276 UNS S31803, ASTM A479 UNS S32205, ASTM A276 UNS S32205, ASTM A479 UNS S31803.
  • Thickness: 50 mm to 6000 mm Long.
  • Type: Duplex Steel Bar.
  • Form: Duplex 2205 Round Bar, Duplex 2205 Hex Bar, Duplex 2205 Flat Bar, Duplex 2205 Square Bar.
  • Length: Single Random, Double Random & Cut Length.
  • Finish: Bright and Black Finish.
  • Origin: Indian Origin, European Origin, Japanese Origin.
  • Testing and Documents: Mill Test Certificates, EN 10204 3.1, Chemical Reports, Mechanical Reports, Destructive Test Report, Non Destructive Test Reports, PMI Test Reports, Visual Inspection Reports, Third Party Inspection Reports, NABL Approved Lab Reports.
  • Packing: Packed in Wooden Boxes, Bubble wraps, Steel Strips Bundled, or as per Customers Requests.

Duplex 2205 Round Bar Sizes in Stock

Material Diameter Length Make
Duplex 2205 Round Bar, Duplex 2205 Flat Bar, Duplex 2205 Hex Bar, Duplex 2205 Square Bar. 0.5 mm to 500 mm 50 mm to 6000 mm Long Indian, European and Japanese origin

Forms of Duplex Steel Bars in Stock

IN STOCK

Duplex Steel Round Bar

Duplex 2205 Round Bars available in 0.5 mm to 500 mm Diameter.

IN STOCK

Duplex Steel Hex Bar

Duplex 2205 Hex Bar with ASTM A276/A479 UNS S31803/S32205.

IN STOCK

Duplex Steel Flat Bar

Duplex 2205 Flat Bar Manufacturer ASTM A276/A479 UNS S31803/S32205.

Types of Duplex S31803/S32205 Bars / Rods

Duplex S31803/S32205 Bright Bar in Stock Duplex S31803Bright Bar
S32205 Duplex Bright Bar
Duplex Steel S31803 Bright Bar
UNS S31803 SS Bright Bar
WERKSTOFF NR. 1.4462 Bright Bar
ASTM A276 2205 Duplex Bright Bar
Duplex S31803/S32205 Hex Bar in Stock Duplex S31803 Hex Bar
S32205 Duplex Hexagonal Bar
S31803 Duplex Steel Hex Bar
UNS S32205 Duplex Steel Hexagonal Bar
ASTM A276 S32205 Duplex Steel Hex Bar
Duplex S31803/S32205 Square Bar in Stock Duplex S31803 Square Bar
S32205 Duplex Square Bars
Duplex Stainless Steel 2205 Square Bar
UNS S32205 Duplex Square Bar
WERKSTOFF NR. 1.4462 Square Bar
ASTM A276 S31803 Duplex Stainless Steel Square Bars
Duplex S31803/S32205 Rectangular Bar in Stock Duplex S32205 Rectangular Bar
S31803 Duplex Rectangular Bars
S32205 Duplex Steel Rectangular Bar
UNS S31803 Duplex Rectangular Bars
WERKSTOFF NR. 1.4462 Rectangular Bar
ASTM A276 S31803 Duplex Stainless Steel Rectangular Bar
Duplex S31803/S32205 Flat Bars in Stock Duplex S31803 Flat Bar
S32205 Duplex Flat Bars
S31803 Duplex Steel Flat Bars
UNS S32205 Duplex Steel Flat Bars
WERKSTOFF NR. 1.4462 Flat Bars
ASTM A276 S32205 Duplex Stainless Steel Flat Bars
Duplex S31803/S32205 Polished Bar in Stock Duplex S32205 Polished Bar
S31803 Duplex Polished Bars
2205 Duplex Stainless Steel Polished Bar
UNS S31803 Duplex Polished Bars
WERKSTOFF NR. 1.4462 Polished Bar
ASTM A276 S31803 Duplex Steel Polished Bar
Duplex S31803/S32205 Threaded Bar in Stock Duplex S31803 Threaded Bar
S32205 Duplex Threaded Bars
S31803 Duplex Steel Threaded Bar
UNS S32205 Duplex Steel Threaded Bar
WERKSTOFF NR. 1.4462 Threaded Bar
ASTM A276 S31803 Duplex Stainless Steel Threaded Bar

S31803/S32205 Duplex Round Bar Chemical Composition

Grade C Mn Si P S Cr Mo Ni N Fe
Duplex S31803 0.030 max 2.00 max 1.00 max 0.030 max 0.020 max 22.0 – 23.0 3.0 – 3.5 4.50 – 6.50 0.14 – 0.20 63.72 min
Duplex S32205 0.030 max 2.00 max 1.00 max 0.030 max 0.020 max 21.0 – 23.0 2.5 – 3.5 4.50 – 6.50 0.8 – 0.20 63.54 min

Duplex S31803/S32205 Rods Mechanical Properties

Grades Density (g/cm 3) Density (lb/in 3) Melting Point (°C) Melting Point (°F)
S31803 / S32205 7.805 0.285 1420 – 1465 2588 – 2669

Equivalent Grades for S31803/S32205 Duplex Round Bar

STANDARD WERKSTOFF NR. UNS
Duplex S31803/S32205 1.4462 S31803 / S32205

Duplex S31803/S32205 Bars Price List

  • 2205 Duplex steel bars
    US $1000-2500 / Ton
  • astm a276 Duplex s31803 rods
    US $2000-3000 / Ton
  • Duplex steel hex bar s32205
    US $1.5-4.5 / Kilogram
  • ASTM A276 2205 Duplex  round bar
    US $1800-2300 / Ton
  • Duplex steel 2205 square bar
    US $1550-2400 / Ton
  • uns s31803 Duplex steel bar manufacturer
    US $1800-2300 / Ton
  • ASTM A276 duplex stainless steel s32205 rods
    US $1300-2600 / Metric Ton
2205 is a (two phase) ferritic/austenitic stainless steel with high strength and excellent corrosion resistance, as supplied in the annealed condition with a maximum brinell hardness of 290 (Rc31).Characterised by high yield strength, double that of the standard austenitic stainless steel grades, good fatigue strength plus excellent resistance to stress corrosion cracking, crevice, pitting, erosion and general corrosion in severe environments. Again generally out performing the standard austenitic stainless steel grades. 2205 cannot be hardened by thermal treatment, but strength and hardness can be increased substantially by cold working, with subsequent reduction in ductility.It is used extensively by the Marine, Chemical, Petrochemical, Pulp and Paper, Oil and Gas, Transport and allied processing industries.

Typical uses are: Anchor Guides, Conveyors, Fasteners, Bushings, High Strength Pump Shafts, Propellor Shafts, plus various applications currently using standard austenitic stainless steel grades.

Material Magnetic due to its part ferritic structure.

 

Colour Code Stocked Sizes
Fluro Orange
(Bar end)
Stock Sizes 25.4 mm to 255 mm diameter.
Bar Finish
Peeled, Turned
Centreless Ground.
Related Specifications
Germany W.Nr 1.4462 DIN X2CrNiMoN22 5 3
USA ASTM A276-98b UNS S31803
Chemical Composition
Min. % Max %
Carbon 0 0.03
Silicon 0 1.00
Manganese 0 2.00
Nickel 4.50 6.50
Chromium 21.00 23.00
Molybdenum 2.50 3.50
Nitrogen 0.08 0.20
Phosphorous 0 0.03
Sulphur 0 0.02
Mechanical Property Requirements - Annealed (As Supplied) to ASTM A276-98b UNS S31803 for Hot and Cold Finished
Temsile Strength Mpa Min. 620
0.2% Yield Strength Mpa Min. 448
Elongation in 50mm % Min. 25
Hardness HB Max 290
Typical Mechanical Properties at room temperature - Annealed
Temsile Strength Mpa 650 - 900
Yield Strength Mpa 570
Elongation in 50mm % 30
Impact Charpy J 130
Hardness HB 235
Rc 23
Elevated Temperature Properties*
While the oxidation resistance of 2205 is good at high temperature as with other duplex stainless steel grades, it is subject to embrittlement when exposed to temperatures above 300oC even for short periods. It is subject to embrittlement at 475oC when exposed for 2 hours only, also between 370oC and 540oC over a longer period.Precipitation of sigma phase will also occur above 650oC resulting in decreased ductility and corrosion resistance. *2205 is therefore not recommended for use at temperatures above 300oC. 
Typical Mechanical Properties at Elevated Temperatures for 63.5 mm Dia Section - Annealed Condition
Test Temperature oC 315 370 480
Temsile Strength Mpa 650 640
Yield Strength Mpa 390 375
Charpy V Notch Impact
After 100 Hours at Temp J
45 22 5
N.B. Should embrittlement occur then annealing is required to rectify.
Low Temperature Properties
2205 is not recommended for use at temperatures below -50oC, again due to its embrittling effect resulting in low ductility.N.B. Unlike high temperature exposure however, the embrittling effect of low temperature exposure is not permanent, existing only for the duration at low temperature.
Typical Charpy V-Notch Impact Properties at Low and Sub Zero Temperatures
Test Temperature oC 25 0 -20 -45
Impact Test Charpy V-Notch 160 60 30 15
Bending
Cold Bending
Cold bending will be extremely difficult due to the high yield strength. Any cold working causing more than 10% deformation should be followed by annealing.
Hot Bending
Hot bending should be performed at 950oC - 1000oC followed by annealing.
Corrosion Resistance
General Corrosion
2205 has superior resistance to general corrosion in most media than 316L or 317L austenitic stainless steel grades
Stress Corrosion Cracking
2205 has a much higher resistance to stress corrosion cracking than 304L or 316L austenitic stainless steel grades.
Pitting Corrosion / Crevice Corrosion
2205 has a higher resistance to pitting corrosion than 316L or 317L austenitic stainless steel grades.
Crevice Corrosion
2205 has a higher resistance to crevice corrosion and erosion corrosion than 316L austenitic stainless steel grade.
Corrosion Fatigue
2205 has better fatigue strength in corrosive environments than the standard austenitic stainless steel grades due to its higher strength and higher corrosion resistance.N.B. For optimum corrosion resistance, surfaces must be free of scale and foreign particles. Finished parts should be passivated. 
Forging
Heat uniformly to 1150oC. Hold until temperature is uniform throughout the section.Do not forge below 900oC. Finished forgings should be air cooled.Finally forgings will require to be annealed in order to obtain optimum mechanical properties and corrosion resistance.

 

Heat Treatment
Annealing
Heat to 1020oC - 1100oC. Hold until temperature is uniform throughout the section. *Soak as required.Quench in water to obtain optimum corrosion resistance. *Actual soaking time should be long enough to ensure that the part is heated thoroughly throughout its section to the required temperature, 30 minutes per 25mm of section may be used as a guide.Please consult your heat treater for best results.

 

Machining
The machinability of 2205 in the annealed as supplied condition is lower than either 304 and 316 due to it's higher yield strength (approximately double).Typically 80% as machinable as the standard 304 and 316 grades, but lower against the improved machinability 304 and 316 grades. N.B. All machining should be carried out as per machine manufacturers recommendations for suitable tool type, feeds and speeds. 
Welding
2205 is readily weldable by the various standard electric arc welding processes.Oxcyacetylene welding is however not recommended due to the possibility of carbon pick up in the weld area.
Welding Procedure
Welding of 2205 should always be carried out using duplex stainless electrodes* similar to the parent metal.No pre-heat or post-heat is required. Post weld annealing, while not necessary for many applications, will however provide optimum corrosion resistance in severe service conditions.*Please consult your welding consumables supplier.

 

Technical Metal Corporation believes the information provided is accurate and reliable. However no warranty of accuracy, completeness or reliability is given, nor will any responsibility be taken for errors or omissions.

316L due to its low carbon content has greater resistance to intergranular corrosion than all the austenitic stainless steel grades except 304L grade and 321 titanium stabilized grade.

Give us a call today to get all the information, +91-98210 71212, If you're looking to buy or sell Stainless Steel Round Rod/Bar, we can help., call to our Distributor in India or mail us to sales@technicalmetalcorp.com for instant free quote of Stainless Steel Round Rod/Bar

OUR CLIENTS IN Mumbai, Chennai, Bengaluru, Pune, Ahmedabad, Houston, Dubai, Singapore, Hyderabad, Navi Mumbai, Bangkok, Jakarta, Vadodara, Seoul, London, Kuala Lumpur, New Delhi, Abu Dhabi, Tehran, Doha, Madrid, Calgary, Riyadh, Istanbul, Kolkata, Coimbatore, Pimpri-Chinchwad, Dammam, Perth, Busan, Santiago, Noida, Milan, Mexico City, Al Jubail, Sydney, Gurgaon, Sao Paulo, Karachi, Sharjah, Edmonton, Jeddah, Lahore, Melbourne, Ho Chi Minh City, Surabaya, Lagos, Toronto, Bogota, Hong Kong, Kochi, Osaka, Montreal, Cairo, Ajman, Manama, New York, Warsaw, Surat, Buenos Aires, Indore, La Victoria, Chicago, Baku, Ulsan, Tiruchirappalli, Islamabad, Pattaya City, Rio de Janeiro, Chandigarh, Vung Tau, Ankara, Los Angeles, Thane, Medan, Lucknow, Bhopal, Shah Alam, Baton Rouge, Minato, Vasai, Batam, Brisbane, Jaipur, Vancouver, Aberdeen, Faridabad, Yokohama, Monterrey, Dallas, San Antonio, Hanoi, Nashik, Paris, Zagreb, Tel Aviv-Yafo, Quezon City, Bhubaneswar, Mississauga, Alexandria, Kobe, Bucharest, Tunis, New Cairo City, Budapest, Visakhapatnam, San Donato Milanese, Rome, Johor Bahru, Tulsa, Quito, Hamilton, Ciudad del Carmen, Saint Petersburg, Cape Town, Ankleshwar, Vienna, Gimhae-si, Amsterdam, Auckland, Chuo, The Woodlands, Sofia, Seville, Tangerang, Petaling Jaya, Cebu City, Krakow, Gdansk, Sandton, Al Khobar, Adelaide, Berlin, Giza, Mashhad, Genoa, Rotterdam, Makati, Dhahran, Izmir, Phoenix, New Orleans, Belgrade, Laem Chabang, Ras Al-Khaimah, Quebec City, Regina, Prague, Copenhagen, Barcelona, Kuantan, Muntinlupa, Moscow, Washington, Seattle, Milwaukee, Caracas, Tallinn, Minsk, Brno, Frankfurt, Lyon, Birmingham, Sheffield, Cilegon, Patna, Anand, Rajkot, Baghdad, Chiyoda, Colombo, Casablanca, Kota Kinabalu, Lisbon, Kyiv, Pasadena, Kalyan, Stavanger, Vaughan, Essen, Guwahati, Kolhapur, Nagpur, Haifa, Atyrau, Ansan-si, Santiago de Queretaro, Kuching, The Hague, Plock, Port-of-Spain, Cleveland, Portland, Pittsburgh, Austin, Johannesburg, Puchong, Vapi, Ambernath, Thoothukudi, Kaunas, Accra, Pengerang, Oslo Municipality, Rosario, Wednesbury, Bekasi, Rawalpindi, Ploiesti, Denver, Boston, Greenville